耐诺钇稳定氧化锆珠(NanorZr-95)：

    耐诺钇稳定氧化锆珠(NanorZr-95)采用高端的钇稳定氧化锆粉做原料，**的电解液中高压滴定成形，中温焙烧定相的工艺制成。氧化锆晶粒直径<0.5μm 保证了珠子细腻和致密的微观结构，使介质具有珍珠般的色泽和光滑工作球面，同时抗剪切性、耐磨性、耐酸碱性**。0.1mm， 0.2mm和0.3mm小粒径的珠子是纳米级研磨的**选择。

氧化锆含量: 95%,             氧化钇含量: 5%,

比      重: >6.0kg/dm³,       散      重: >3.6kg/L,

莫 氏 硬度: 9,                 维 氏 硬度: >1200kg/mm²,

弹 性 模量: 200Gpa,         颜      色: 奶白,     

粒      径: 0.05-3.2mm,        包      装: 25kg/桶.

NanorZr-95 yttria stabilized zirconium oxide bead is shaped with cutting-edge dropping method for small sizes and granulating method for big sizes. The high grade raw material and the leading know-how guarantee the compact microstructure with less 0.5μm polycrystal of Y-TZP, which give transparent and full sphericity to the bead. The excellent share resistance, wear resistance and acid & alkali resistance can be used full of applications. The small sizes 0.1mm, 0.2mm and 0.3mm is the best choice for grinding the nanometer products in high energy density bead mill with contamination free way.

ZrO₂ %: 95 ,                    Y₂O₃ %: 5

Density: >6.0kg/dm³,             Bulk Density: >3.6kg/L

Hardness Vickers: >1300kg/mm²     Toughness: 10Mpa.m1/2,

Crushing Strength: 2300N (2mm)   Color: off white

Sizes: 0.1-3.2mm ,               Packing: 25kg/pail