耐诺碳化钨珠(Nanor-WC）

耐诺碳化钨珠Nanor-WC由全球**的的滴定滚动工艺成型，在真空电炉中无氧烧结而成。致密的晶相结构造就了珠子至高的密度和耐磨性，为超硬材料纳米级研磨提供了高能量的微珠，是研磨介质微珠行业革命性的创造。

碳化钨含量: 85%,                 氧化钴含量: 15%,

比      重: >14.5kg/dm³,         散      重: >8.6kg/L,

莫 氏 硬度: 9.5,        维 氏 硬度: >1500kg/mm²,

断 裂 韧性: 15Mpa.m1/2       弹 性 模量: >710Gpa,

粒      径: 0.2-2.2mm,             颜      色: 黑色,           

Nanor-WC cemented carbide bead is shaped with cutting edge dropping & rolling method and is sintered in the 

vacuum kiln. The compact microstructure of bead offer the bead the highest density and wear resistance. It is a 

creative invention of grinding media special in small sizes for nano sizes grinding.

WC %: 85 ,                        Co %: 15

Density: >14.5kg/dm³,               Bulk Density: >8.6kg/L

Hardness Vickers: >1500kg/mm²,      Elasticity Module: >710GPa^1/2  

Crushing Strength: 2000N (2mm)，    Sizes: 0.2-2.2mm ,