耐诺硅酸锆珠(NanorZr-64):耐诺硅酸锆珠(NanorZr-64)采用进口高纯度的锆英砂为原材料,专利的滚动法的成型,中温烧结的工艺制成。珠内由致密的硅酸锆微粒组成微观结构,拒绝了毛隙和空腔,比同类珠子有更大的密度、硬度和饱满的球形度,磨耗率是同类硅酸锆珠的50%。中等的密度和硬度适合中低粘度浆料的分散和研磨,是盘式砂磨机**的配置。氧化锆含量:64%,氧化硅含量:33%,比重:>4.0kg/dm3,散重:>2.5kg/L,莫氏硬度:>7.0,维氏硬度:>900kg/mm2,耐压强度:1200N(2mm),粒径:0.4-12.0mm,吨磨耗:<0.05kg/吨,包装:25kg/桶NanorZr-64zirconiumsilicatebeadismadefromhighpurezirconsand,granulatedinapatentwayandhardenedatamiddletemperaturekilin.ComparedtotheotherzirconbeadsandtheATZbeads,ithashomogeneousmicrostructureandnoairpockets.Thisgivethem50%lowerbeadswearthantheothers.Themiddledensityandhighercrushingstrengthfeaturesaresuitabletogrindingslurryinviscosityfromlowtomiddle.Itisthebestpartnerofdisctypebeadmill.ZrO2%:64,SiO2%:33Density:>4.0kg/dm3,BulkDensity:>2.5kg/LHardnessVickers:>900kg/mm2,CrushingStrength:1200N(2mm),Sizes:0.4-12.0mm,Packing:25kg/pail