耐诺铈稳定氧化锆珠(NanorZr-Ce):耐诺铈稳定氧化锆珠(NanorZr-Ce)采用稀土氧化铈作稳定剂,全球**的电解液中高压滴定成型,中温烧结定相的工艺制成。饱满的球度和狭窄粒径分布为其外观特征,珠子的微观结构为均匀致密的四方氧化锆微晶构成,使其具有宝石般的硬度和密度,是所有锆系列磨介中*重的一种。优异的断裂韧性和超低磨耗特别适合对高固相、高磨蚀和高粘度的物料的分散和研磨。相对钇稳定氧化锆珠比较低的硬度,可以很好避免对砂磨机接触件的磨损。氧化锆含量:80%,氧化铈含量:20%,比重:>6.1kg/dm3,散重:>3.8kg/L,莫氏硬度:9,维氏硬度:>1100kg/mm2,断裂韧性:15Mpa.m1/2弹性模量:180Gpa,吨磨耗:0.01kg/干吨,粒径:0.3-5.5mm,颜色:棕色,包装:25kg/桶CeriastabilizedzirconiabeadNanorZr-Ceisshapedinahighpressuredroppingsystemandsinteredinamiddletemperature,whichistheleadingmanufacturingprocessintheworld.Thecompactandhomogenoustetragonalzirconiapolycrystalresultinthehighesthardness,densityandexcellentwearresistance.Itisoptimalformillinghighviscosityandabrasionparticlesinhighenergyintensitybeadmills.Comparedtotheyttriastabilizedbead,thelowerhardnessmeansthatitprotectsthecontactedpartsofmill.ZrO2:80%CeO2:20%Density:>6.1kg/dm3BulkDensity:>3.8kg/LHardnessVickers:>1100kg/mm2CrushingStrength:2000N(2mm)Toughness:20Mpa.m1/2WearRate:<0.01kg/TSizes:0.3-5.5mmPacking:25kg/pail