硅酸锆珠(CZS):采用电解液中滴定成型,高温烧结定相的先进工艺制成。珠内由致密的硅酸锆微粒组成微观结构,拒绝了毛隙和空腔,避免了晶相和玻璃相的分离,比同类珠子有更大的密度和硬度,磨耗率是同类硅酸锆珠的1/2。中等的密度和硬度适合中低粘度浆料的分散和研磨,可匹配**部分的砂磨机,为通用型磨介。氧化锆含量:64%,氧化硅含量:33%,比重:>4.0kg/dm3,散重:>2.5kg/L,莫氏硬度:>7.0,维氏硬度:>900kg/mm2,耐压强度:1200N(2mm),粒径:0.4-3.2mm,吨磨耗:0.05kg/吨,包装:25kg/桶CZSzirconiumsilicatebeadsareshapedinelectrolytesolutionandhardenedatahightemperatureinkilin.ComparedtotheotherzirconbeadsandtheATZbeads,theyhavehomogenousmicrostructureandnoairpockets.Thisgivethem1/2lowerbeadswearthantheothers.Themiddledensityandhighcrushingstrengthfeaturesaresuitabletogrindingslurryinvisicosityfromlowtomiddleinmorekinfofbeadsmills.ZrO2%:64,SiO2%:33Density:>4.0kg/dm3,BulkDensity:2.56kg/LHardnessVickers:>900kg/mm2,CrushingStrength:1200N(2mm),Sizes:0.4-5.5mm,Packing:25kg/bucket