耐诺碳化钨珠(Nanor-WC）耐诺碳化钨珠Nanor-WC由全球**的的滴定滚动工艺成型，在真空电炉中无氧烧结而成。致密的晶相结构造就了珠子至高的密度和耐磨性，为超硬材料纳米级研磨提供了高能量的微珠，是研磨介质微珠行业革命性的创造。碳化钨含量:85%,氧化钴含量:15%,比重:>14.5kg/dm3,散重:>8.6kg/L,莫氏硬度:9.5,维氏硬度:>1500kg/mm2,断裂韧性:15Mpa.m1/2弹性模量:>710Gpa,粒径:0.2-2.2mm,颜色:黑色,Nanor-WCcementedcarbidebeadisshapedwithcuttingedgedropping&rollingmethodandissinteredinthevacuumkiln.Thecompactmicrostructureofbeadofferthebeadthehighestdensityandwearresistance.Itisacreativeinventionofgrindingmediaspecialinsmallsizesfornanosizesgrinding.WC%:85,Co%:15Density:>14.5kg/dm3,BulkDensity:>8.6kg/LHardnessVickers:>1500kg/mm2,ElasticityModule:>710GPa1/2CrushingStrength:2000N(2mm)，Sizes:0.2-2.2mm,